Spring steel is a name given to a wide range of steels[1] used in the manufacture of different products, including swords, saw blades, springs and many more. These steels are generally low-alloy manganese, medium-carbon steel or high-carbon steel with a very high yield strength. This allows objects made of spring steel to return to their original shape despite significant deflection or twisting.
See also: Steel grades |
Many grades of steel can be hardened and tempered to increase elasticity and resist deformation; however, some steels are inherently more elastic than others:
SAE grade (ASTM grade) |
Composition | Yield strength | Hardness (HRC) | Comments | |
---|---|---|---|---|---|
Typical | Maximum | ||||
1070 | 0.65-0.75% C, 0.60-0.90% Mn, max .050% S, max .040% P | Normally supplied annealed | 165vpn | 180vpn | CS70, CK67, C70E |
1074/1075[2] | 0.70–0.80% C, 0.50–0.80% Mn, max. 0.030% P, max. 0.035% S[3] | 62–78 ksi (430–540 MPa)[4] | 44–50[5] | 50 | Scaleless blue, or Polished Bright |
1080 (A228) | 0.7–1.0% C, 0.2–0.6% Mn, 0.1–0.3% Si[6] | Piano wire, music wire, springs, clutch discs | |||
1095 (A684)[2] | 0.90–1.03% C, 0.30–0.50% Mn, max. 0.030% P, max. 0.035% S[7] | 60–75 ksi (410–520 MPa), annealed | 48–51[5] | 59 | Blue, or polished bright spring steel |
5160 (A689)[8] | 0.55–0.65% C, 0.75–1.00% Mn, 0.70–0.90% Cr[9] | 97 ksi (670 MPa) | 63 | Chrome-silicon spring steel; fatigue-resistant | |
50CrV4 (EN 10277) | 0.47–0.55% C, max. 1.10% Mn, 0.90–1.20% Cr, 0.10–0.20% V, max. 0.40% Si | 170 ksi (1,200 MPa) | Old British 735 H1steel, SAE 6150, 735A51 | ||
9255 | 0.50–0.60% C, 0.70–0.95% Mn, 1.80–2.20% Si[9] | ||||
301 spring-tempered stainless steel[10] |
0.08–0.15% C, max. 2.00% Mn, 16.00–18.00% Cr, 6.00–8.00% Ni[9] | 147 ksi (1,010 MPa) | 42 | Equivalents EN 10088-2 1.4310, X10CrNi18-8 |